Zinc oxide thin films were deposited by chemical spray pyrolysis onto glass substrates which are held at a temperature of 673 K. Some structural, electrical, optical and gas sensing properties of films were studied. The resistance of ZnO thin film exhibits a change of magnitude as the ambient gas is cycled from air to oxygen and nitrogen dioxide

The presence of heavy metals in the environment is major concern due to their toxicity. In the present study a strong acid cation exchange resin, Amberlite IR 120 was used for the removal of lead, zinc and copper from simulated wastewater. The optimum conditions were determined in a batch system of concentration 100 mg/L, pH range between 1 and 8, contact time between 5 and 120 minutes, and amount of adsorbent was from 0.05 to 0.45 g/100 ml. A constant stirring speed, 180 rpm, was chosen during all of the experiments. The optimum conditions were found to be pH of 4 for copper and lead and pH 6 for zinc, contact time of 60 min and 0.35 g of adsorbent. Three different temperatures (25, 40 and 60°C) were selected to investigate the effect

A simple, sensitive and accurate spectrophotometric method has been developed for the determination of salbutamol sulphate (SAB) and isoxsuprine hydrochloride (ISX) in pure and pharmaceutical dosage. The method involved oxidation of (SAB) and (ISX) with a known excess of N-bromosuccinamid in acidic medium, and subsequent occupation of unreacted oxidant in decolorization of Evans blue dye (EB). This, in the presence of SAB or ISX was rectilinear over the ranges 1.0-12.0, 1.0-11.0 µg/mL, with molar absorptivity 4.21×10⁴ and 2.58×10⁴ l.mol^-1.cm^-1 respectively. The developed method had been successfully applied for the determination of the studied drugs in their pharmaceutical dosage resulting i

The aim of this paper was to investigate the removal efficiencies of Zn⁺² ions from wastewater by adsorption (using tobacco leaves) and forward osmosis (using cellulose triacetate (CTA) membrane). Various experimental parameters were investigated in adsorption experiment such as: effect of pH (3 - 7), contact time (0  - 220) min, solute concentration (10 - 100) mg/l, and adsorbent dose (0.2 - 5)g. Whereas for forward osmosis the operating parameters studied were: draw solution concentration (10 - 150) g/l, pH of feed solution (4 - 7), feed solution concentration (10 - 100) mg/l. The result showed that the removal efficiency by using adsorption was 70% and the removal efficiency by using forward osmosis was 96.2 %. 

The CIGS/CdS p-n junction thin films were fabricated and deposited at room temperature with rate of deposition 5, and 6 nm secG1 , on ITO glass substrates with 1mm thickness by thermal evaporation technique at high vacuum pressure 2×10G5 mbar, with area of 1 cm2 and Aluminum electrode as back contact. The thickness of absorber layer (CIGS) was 1 µm while the thickness of the window layer CdS film was 300 nm. The X-ray Diffraction results have shown that all thin films were polycrystalline with orientation of 112 and 211 for CIGS thin films and 111 for CdS films. The direct energy gaps for CIGS and CdS thin films were 1.85 and 2.4 eV, respectively. Atomic Force Microscopy measurement proves that both films CIGS and CdS films have nanostru

Ameloblastic carcinoma is a rare malignant odontogenic tumor that is further classified into being primary or secondary arising from a preexisting benign ameloblastoma. It affects the mandible in two thirds of the patients. there is no standard treatment protocol for this lesion but radical surgical excision with or without radiotherapy is reported in the majority of cases. In this paper we present a case of a 60 year old female diagnosed with ameloblastic carcinoma of the mandible that was treated by radical resection of the mandible with selective neck dissection and postoperative radiotherapy.