The effect of the concentration of the colloidal nanomaterial on their optical limiting behavior is reported in this paper. The colloids of sliver nanoparticles in deionized water were chemically prepared for the two concentrations (31 ppm and 11ppm). Two cw lasers (473 nm Blue DPSS laser and 532 nm Nd:YAG laser) are used to compare the optical limiting performance for the samples. UV–visible spectrophotometer, transmission electron microscope (TEM) and Fourier Transformation Infrared Spectrometer (FTIR) were used to obtain the characteristics of the sample. The nonlinear refractive index was calculated to be in the order of 10-9 cm2/W. The results demonstrate that the observed limiting response is significant for 532nm. In addition, t

Carbon nanoparticles are prepared by sonication using carbon black powder. The surface morphology of carbon black (CB) and carbon nanoparticles (CNPs) is investigated using scanning electron microscopy (SEM). The particles size ranges from 100 nm to 400 nm for CB and from 10 nm to 100 nm for CNPs. CNPs and CB are mixed with silicon glue of different ratios of 0.025, 0.2, 0.05, and 0.1 to synthesis films. The optical properties of the prepared films are investigated through reflectance and absorbance analyses. The ratio of 0.05 for CNPs and CB is the best for solar paint because of its higher solar water heater efficiency and is then added to the silicon glue . Temperature of cold water and temperature of hot water in storage tank were ta

In order to achieve optimal plant growth and production, essential nutrients must be readily available in adequate quantities and in a balanced proportion to give a good yield, especially broccoli which has health benefits that may not be found in many other plants. For this purpose, this experiment was carried out during the seasons 2019/2020 in the botanical garden of the Department of Biology, College of Science for Women, University of Baghdad, to study the effects of nitrogen and sulphur and their interaction on eight parameters reflecting the overall traits of vegetative growth, yield, and chlorophyll content of broccoli Brassica oleracea L. (var. italic JASSMINE F1 Hybrid). A factorial design with three replicates was use

Background and Aim: The use of food dyes can cause certain diseases, such as anemia and indigestion, along with other disorders, tumors, and even cancer. Therefore, this study aimed to determine the chemical nature and toxicity of some commercial dyes locally used in processed foods compared with standard food dyes. Materials and Methods: Three types of standard and commercial food color additives (Sunset Yellow, Tartrazine, and Carmoisine) were extensively examined. The chemical structures and functional groups of the dyes were evaluated by Fourier-transform infrared (FTIR) spectroscopy. The melting temperatures of the dyes were also determined by chemical thermal analysis. The acute toxicity test to evaluate the standard and commercial

In this study, silver nanoparticles (AgNPs) were synthesized using a cold plasma technique and a plasma jet. They were then used to explore how photothermal treatment may be used to treat lung cancer (A549) and normal cells (REF) <i>in vitro</i>. The anti-proliferative activity of these nanoparticles was studied after A549 cells were treated with (AgNPs) at various concentrations (100&#37;, 50&#37;, or 25&#37;) and exposure times (6 or 8 min) of laser after 1 h or 24 h from exposed AgNPs. The highest growth inhibition for cancer cells is (75&#37;) at (AgNPs) concentration (100&#37;) and the period of exposure to the laser is (8 min). Particle size for the prepared samples varied according to the diameter o

In this work, pure and Ag-doped nickel oxide (NiO) thin films were deposited on glass substrates with different dopant concentrations (0.1, 0.2, 0.3 and 0.4 wt.%) by pulsed-laser deposition (PLD) technique at room temperature. These films were annealed at temperature of 450 °C. The structural and optical properties of the prepared thin films were studied. It was found that annealing process has lead to increase the transmittance of the deposited films. Also, the transmittance was found to increase with doping concentration of silver in the deposited NiO films. The optical energy gap was decreased from 3.5 to 3.2 eV as the doping concentration was increased to 0.4 %.