In the present work, lead silicate glasses have been prepared with
different amount of lead oxide content. Structure properties such as
X-ray diffraction, AFM, and FTIR analyses have been done. The
exceeding of PbO content more than 25wt% revealed a decreasing in
density. The X- ray revealed that the strongest peak related to
Hexagonal silica dioxide and the other crystal phases formed were
related to silica oxide (SiO2) and lead oxide (PbO). Growth and
decayed phases in X-ray have been observed with changing lead
oxide content. Homogeneous surface was obtained using AFM
analyzer with an average diameter around 100 nm. Infrared spectrum
is characterized by the presence of large absorption band between
120

Five levels of Zn-EDTA fertilizer and foliar application of boron were used to study the local rice response through studying of some vegetative and reproductive growth characters, by conducting two field experiments at Kanipanka Agricultural Research Station during the summer season of 2004 by using RCBD with three replications. Significant differences were found in studied characters, there were increase in the number of days from seeding to 50% flowering (94.330-96.233) days, from 50% flowering to physiological maturity (37.50-38.28) days, plant height (82.50-91.423) cm and LAI (5.441-7.525). Reproductive characters such as number of grains panicle-1 (74.11-85.88), number of panicles m-2 (321.00-426.083), biological yield (8166.166-11082

A laboratory experiment was carried out according to a completely randomized design with four repetitions on the seeds resulting from a field experiment applied for the two seasons, 2020 and 2021, to find out the effect of the cultivars (Ambar 33, Yasamin, Dijlah, Ambar Al-Baraka and Furat 1) and the harvest dates (at physiological maturity and after 7 and 14, 21 and 28 days of physiological maturity) on the vigour of rice seeds. The results showed the superiority of the seeds of the cultivar Anbar Al-Baraka at first and final counting, dry weight of the seedling, seedling vigor index and electrical conductivity, and the superiority of the seeds of Dijla cultivar at accelerated aging test and cold test without significant difference with th

The current study was designed to remove Lead, Copper and Zinc from industrial wastewater using Lettuce leaves (Lactuca sativa) within three forms (fresh, dried and powdered) under some environmental factors such as pH, temperature and contact time. Current data show that Lettuce leaves are capable of removing Lead, Copper and Zinc ions at significant capacity. Furthermore, the powder of Lettuce leaves had highest capability in removing all metal ions. The highest capacity was for Lead then Copper and finally Zinc. However, some examined factors were found to have significant impacts upon bioremoval capacity of studied ions, where best biosorption capacity was found at pH 4, at temperature 50º C and contact time of 1 hour.

            The development of a new, cheap, efficient, and ecofriendly adsorbents has become an important demand for the treatment of waste water, so nano silica is considered a good choice. A sample of nanosilica (NS) was prepared from sodium silicate as precursor and the nonionic surfactant Tween 20 as a template. The prepared sample was characterized using various characterization techniques such as FT-IR, AFM, SEM and EDX analysis. The spectrum of FTIR confirms the presence of silica in the sample, while SEM analysis of sample shows nanostructures with pore ranging (2-100nm).The adsorptive properties of this sample were studied by removing Congo red dye (CR) from aqueous solution. Batch experimental methods were carried o

Cladophora and Spirulina algae biomass have been used for the removal of Tetracycline (TC) antibiotic from aqueous solution. Different operation conditions were varied in batch process, such as initial antibiotic concentration, different biomass dosage and type, contact time, agitation speed, and initial pH. The result showed that the maximum removal efficiencies by using 1.25 g/100 ml Cladophora and 0.5 g/100 ml Spirulina algae biomass were 95% and 94% respectively. At the optimum experimental condition of temperature 25°C, initial TC concentration 50 mg/l, contact time 2.5hr, agitation speed 200 rpm and pH 6.5. The characterization of Cladophora and Spirulina biomass by Fourier transform infrared (FTIR) indicates that the presenc