In this study, the photodegradation of Congo red dye (CR) in aqueous solution was investigated using Au-Pd/TiO2 as photocatalyst. The concentration of dye, dosage of photocatalyst, amount of H2O2, pH of the medium and temperature were examined to find the optimum values of these parameters. It has been found that 28 ppm was the best dye concentration. The optimum amount of photocatalyst was 0.09 g/75 mL of dye solution when the degradation percent was ~ 96 % after irradiation time of 12 hours, while the best amount of hydrogen peroxide was 7μl/75 mL of dye solution at degradation percent ~97 % after irradiation time of 10 hours, whereas pH 5 was the best value to carry out the reaction at the highest degradation percent. In additio

Abstract

To evaluate the effectiveness of Phenolic Compound of Salvia Frigida on induced atopic dermatitis (AD) of mice. Forty mice were included in the study, divided in to four groups (10 mice/group): apparently healthy, induced AD without treatment, induced AD treated with tacrolimus 0.1% ointment, and induced AD treated with Phenolic Compound of Salvia Frigida cream 5%. Examination of histopathology was done and skin homogenates levels also measured. Levels of WBC, Eosinophil, skin tissue homogenate of IL-13 and IL-4, serum IgE, and histopathological scores were significantly increased among induced non treated AD group in comparison with control group. Comparisons of non-treated induced AD

A new  light-weight nanocarbon prepared by spray-drying method  to obtain  particle size is 21.7 nm based of polylactic acid biodegradable film in antistatic packaging .Bio carbon (biochar) is  obtained from  plants and soils to naturally absorb and store carbon dioxide from the atmosphere . Therefor it has been used to support biodegradable polylactic acid (PLA) with to obtain 100% recyclable material.

Using plasticizer thymol of polylactic acid and biochar (bio carbon) as composites were prepared by a solution casting method with (0.5-10)wt% biochar. The composites  characterized by  FTIR, electrical conductivity, mechanical properties , contact angle and Colar and Brightness . Results show th

This research foxed on the effect of fire flame of different burning temperatures (300, 400 and 500)oC on the compressive strength of reactive powder concrete (RPC).The steady state duration of the burning test was (60)min. Local consuming material were used to mixed a RPC of compressive strength around (100) MPa. The tested specimens were reinforced by (3.0) cm hooked end steel fiber of (1100) MPa yield strength. Three steel fiber volume fraction were adopted in this study (0, 1.0and 1.5)% and two cooling process were included, gradual and sudden. It was concluding that increasing burning temperature decreases the residual compressive strength for RPC specimens of(0%) steel fiber volume fraction by (12.16, 19.46&24.49) and (18.20, 27.77 &3

The current research aims to determine the role of strategic leadership in achieving organizational excellence. In this context the sample of the research consist of 123 managers .The research problem can be summarized as {what is the role of strategic leadership in achieving organizational excellence}which resulted in a number of sub-questions and its goal was to explain the theoretical philosophy and intellectual expositions of this variables because of they are vital variables imposed by the current situation. To achieve research objectives we had use the questionnaire as a tool to collect data and information after verifying the validity and dependency of the measures. A number of statistical techniques and tools had been use