‎ Sixteen new complexes with the general formula [M(L)2(H2O)2] were ‎prepared resulting from the reaction of the two new Schiff base ligands, which ‎are‏: -‏ L1= (E)-5-((2-hydroxybenzylidene)amino)-2-phenyl-2,4-dihydro-3H-pyrazol-3-one)‎ L2 = (E)-5-((2-hydroxy-3-methoxybenzylidene)amino)-2-phenylpyrazolidin-3-one) ‎ ‎ With divalent metal ions (manganese, cobalt, nickel, copper, zinc, cadmium, ‎mercury) and (tetravalent platinum).‎‏ ‏ ‎ Ligands was derived from the reaction of the amine (5-amino-2-phenyl-2,4-‎dihydro-3H-pyrazol-3-one) with Salicylaldehyde and ortho-vanillin, which is ‎linked to the metal ions via the nitrogen atoms are the isomethene group and ‎the oxygen is the hydroxide group of t

Newly 4-amino-1,2,4-triazole-3-thione ring 2 was formed at position six of 2-methylphenol from the reaction of 6-(5-thio1,3,4-oxadiazol-2-yl)-2-methylphenol 1 with hydrazine hydrochloride in the presence of anhydrase sodium acetate. Seven newly fused heterocyclic compounds were synthesized from compound 2. First fused heterocyclic was 6-(6-(3,5-di-tertbutyl-4-hydroxyphenyl)-[1,2,4]triazolo[3,4-b][1,3,4]thiadiazol-3-yl)-2-methylphenol 3 synthesized from reaction compound 2 with 3,5-di-tert-butyl-4-hydroxybenzoic acid in POCl3. Reaction compound 2 with bromophencylbromide afford 6-(6-(4-bromophenyl)-5H-[1,2,4]triazolo[3,4-b][1,3,4]-thiadiazin-3-yl)-2-methylphenol 4. 6-(6-thio-1,7a-dihydro-[1,2,4] triazolo[3,4-b][1,3,4]-thiadiazol-3-yl)-2

The coordination ability of the azo-Schiff base 2-[1,5-Dimethyl-3-[2-(5-methyl-1H-indol-3-yl)-ethyl imino]-2-phenyl-2,3-dihydro-1H-pyrazol-4-ylazo]-5- hydroxy-benzoic acid has been proven in complexation reactions with Co(II), Ni(II), Cu(II), Pd(II) and Pt(II) ions. The free ligand (LH) and its complexes were characterized using elemental analysis, determination of metal concentration, magnetic susceptibility, molar conductivity, FTIR, Uv-Vis, (1H, 13C) NMR spectra, mass spectra and thermal analysis (TGA). The results confirmed the coordination of the ligand through the nitrogen of the azomethine, Azo group (Azo) and the carboxylate ion with the metal ions. The activation thermodynamic parameters, such as ΔE*, ΔH*, ΔS*, ΔG*and K are cal

A series of new heterocyclic aromatic derivatives compounds were synthesized by reacted of Bis-methylene-di-(2-aminobenzoyl chloride) ‎with different chloride moieties such as piperidine-1-sulfonylchloride, Pryidine-3-sulfonylchloride, 4,4and#39;-(diazene-1,2-diyl)dibenzoyl-chloride and chloramphenicol respectively, to afforded a derivatives compound containing primary amine group [A-A4]. These derivative compounds [A-A4] were reacted with polyethanol using cold-warm esterification to synthesize of new graft polymers [B1-B4]. The structures of products were conforming by FT-IR and 1H-NMR spectroscopy. XRD-Diffraction of grafted polymer showed compound [B1 and B3] were crystal and semi-crystal respectively. As well as, derivatives

         This study involves the design of 24 mixtures of fiber reinforced magnetic reactive powder concrete containing nano silica. Tap water was used for 12 of these mixtures, while magnetic water was used for the others. The nano silica (NS) with ratios (1, 1.5, 2, 2.5 and 3) % by weight of cement, were used for all the mixtures. The results have shown that the mixture containing 2.5% NS gives the highest compressive strength at age 7 days. Many different other tests were carried out, the results have shown that the carbon fiber reinforced magnetic reactive powder concrete containing 2.5% NS (CFRMRPCCNS) had higher compressive strength, modulus of rupture, splitting tension, str

One of the most essential components of asphalt pavements is the filler. It serves two purposes. First, this fine-grained material (diameter less than 0.075 mm) improves the cohesiveness of aggregate with bitumen. Second, produce a dense mixture by filling the voids between the particles. Aluminum dross (AD), which is a by-product of aluminum re-melting, is formed all over the world. This material causes damage to humans and the environment; stockpiling AD in landfills is not the best solution. This research studies the possibility of replacing part of the conventional filler with aluminum dross. Three percent of dross was used, 10, 20, and 30% by filler weight. The MarshallMix design method was adopted to obtain the op

The aim of this research is to benefit from recycl the aircraft waste oils which is discarded in sewage network, to be used in preparation of greases for industrial purposes and to reduce the environmental pollution. In this research synthetic greases were prepared with special specifications by mixing the waste oils after treating with (silica gel as adsorbent agent, and filtration to precipitate impurities then heated to 110 C? to get rid of water) bentonite produced in Iraq which is available and cheap with existence of high density polyethylene at specific conditions of ( heating and mixing) . The best weight proportion were reached, then paraffin wax and additives were added to improve the properties of grease and give the

Polyvinyl alcohol, (PVA) was prepared using polyvinyl acetate emulsion (manufactured by Al-Jihad factory,
That-Al-Sawary Company) as a local raw material. In this investigation, polyvinyl acetate emulsion was converted to
solid form by coagulation the polymer from its emulsion using sodium sulphate salt as coagulant aid, then alcoholyzed
the solid polyvinyl acetate in methanol using sodium hydroxide as catalyst, polyvinyl alcohol produced by this method is
a dry, white to yellow powder.
Three affecting variables on the degree of hydrolysis of PVA were studied, these variable are Catalyst to
polymer weight ratio in the range of 0.01 – 0.06, reaction time in the range of 20 – 90 min, and reaction temperature in
the