A tungsten inert gas (TIG) welding is one of the most popular kinds of welding used to join metals mainly for aluminum alloys.  However, many challenges may be met with this kind of joining process; these challenges arise from decay of mechanical properties of welded materials. In the present study, an attempt was made to enhancing the mechanical properties of TIG weld joint of 6061-T6 aluminum alloy by hardening the surfaces using shoot peening technique. To optimize the shoot peening process three times of exposure (5, 10, and 15) min. was used. All peened and unpeened, and welded and unwelded samples were  characterized by metallographic test to indicate the phase transformation and modification in microstructure occurring d

The research deals with an important detail of the joints of the film industry and television drama, which is the expression and aesthetic of the long shot, after being popularized by some directors, and that the long shot has been employed since the beginning of the cinema. But the research addresses the contemporary film and how the long shot worked. The researcher identified her goal in identifying the aesthetic and expressive of the long shot in the contemporary film, and then defined the term of the shot and the long shot.
The theoretical framework was based on two topics: the first (aesthetic and artistic expression in cinema) and the second (the long shot and the state of its construction). The researcher then chose LA LA LAND

في هذا البحث حضر الكاربون المنشط ذو الحجم الحبيبي في المدى المايكروي والمدى النانوي من قشور الجوز واجريت عملية الكربنة باستخدام فرن المايكرويف ومن ثم استعمل محلول (%50) من حامض الفسفوريك مع المادة المكربنة وبأزمان مختلفة (2,4,8,16,24) ساعة لتحديد الزمن الأفضل لعملية التنشيط في هذا البحث ، وبعد ذلك اضيفت نسب وزنية مختلفة من مخلفات بولي بروبلين عند زمن (8) ساعة وكانت النسب 0.05):,1 0.1:,1 0.15:0.2 ,1: (1:0.25 ,1 للمضاف البوليمري ومس

In this study many specimen s were prepared from 2024-T3 Aluminum alloy for corrosion test by the dimensions of (15*15*3) mm according to ASTM G71-31 and then subjected to shot peening process at different time (15, 30, 45) minutes using steel ball having a diameter of 2.75 mm and Rockwell Hardness of 55R_C to induce compressive residual stress which were measured using X-Ray diffraction method, surface roughness and   hardness were tested before and after peening. Electrochemical corrosion test by Tafel extrapolation method was carried out in an environment of 3 .5% NaCl solutions (sea water) where Corrosion rate calculated using Tafle equation.

The obtained results show a favorable influence of SP treatment

The effects of shot peening treatment (SPT) were studied at (10,20, and 30) minutes on the rotating bending fatigue behavior and the behavior of the alloy steel DIN 41Cr4 vibrations. The hardness test, tensile test, constant amplitude fatigue tests, and the vibration measurements were performed on samples with and without cracks at room temperature (RT), also, the fracture surface was examined and analyzed by a Scanning Electron Microscope (SEM). The results of the investigations, for example, Stress to Number of cycles to failure (S-N) curves, fatigue strength improvement factor of 5% to 10%, the decreasing percentage of maximum Fast Fourier Transform (FFT) acceleration of the shot-peened condition were compared to untr

أن أهمية البحث تكمن في أعداد منهج تعليمي مقترح وفق أنموذج بايبي وتعلم مهارتي الاعداد وأستقبال الارسال بالكرة الطائرة للطالبات وتكمن أهمية أنموذج بايبي بالمساعدة على توظيف المعلومات في المواقف المختلفة،وان مشكلة البحث جاءت بعد أطلاع الباحثات على الدراسات والمصادر السابقة لاحظت بأن هناك ضعف في الاداء المهاري في مهارتي الاعداد وأستقبال الارسال بالكرة الطائرة من قبل الطالبات لذلك أرتأت الباحثات الى التع

The traction property is one of the important mechanical properties, especially the rotary parts which are subjected to constant and variable loads There are many methods used to improve this property, and the shoot peening by metal balls is considered the most critical one. the study focuses on this characteristic of steel CK35 used in many engineering applications as the rotating shafts and railway This study shows that the fatigue strength is improved by14% after shoot peening with metal balls. The study includs the rehabilitation of damaged samples as a result of fatigue corrosion. The standard solution adopted was 36% MgCl­₂ with a 30 days immersion period. These samples has been improved by 6% after it decreased by18% d

Abstract

    Corrosion-fatigue occurs by the combined actions of cyclic loading and corrosive environment. The effect of shot peening on cumulative corrosion-fatigue life of 1100-H12 Al alloy was investigated. Before fatigue testing, specimens were submerged in 3.5%NaCl solution for 71 days. Constant fatigue tests were performed with and without corrosive environment. Cumulative corrosion-fatigue tests were also carried out in order to determine the fatigue life before and after shot peening. The constant fatigue life was significantly reduced due to corrosive environment and the endurance fatigue limit was reduced by 13% compared with dry fatigue. In case of shot peening the cumul