SAGD is a thermal recovery process in which steam oil ratio, SOR, is a key parameter that can affect the economic outcome of the process. Reservoirs with underlying or overlying lean bitumen present challenges for SAGD as they can act as a heat sink. Water has higher heat capacity than the bitumen and thus requires more steam to heat up the reservoir leading to higher SOR. The potential outcome of operating SAGD in these conditions may be lower bitumen rate and higher steam injection rate, both of which affect plant throughput and thus the economic matrix of SAGD. This paper looks at the performance of SAGD process in the presence of top lean bitumen. It will examine the theoretical CSOR that is needed to produce the bitumen with different

ZSM-5 zeolite was synthesis under hydrothermal conditions at 175^oC. The synthesis parameters have been investigated to find optimum synthesis method. Firstly, the crystallization time has been investigated to find the optimum crystallization time. Also, the ageing time was studied. The morphology, structure, and composition of the synthesized ZSM-5 zeolite were characterized using scanning electron microscopy (SEM), pH meter, viscometer, and X-ray powder diffraction (XRD). The bulk Si/Al ratio of ZSM-5 zeolite was in the range of 9.5—11.7. The synthesized ZSM-5 zeolite with appropriate ageing time could adjust crystal size and degree of the crystallinity. The crystal size of ZSM-5 zeolite obtained at an agei

NiO0.99Cu0.01 films have been deposited using thermal evaporation
technique on glass substrates under vacuum 10-5mbar. The thickness
of the films was 220nm. The as -deposited films were annealed to
different annealing temperatures (373, 423, and 473) K under
vacuum 10-3mbar for 1 h. The structural properties of the films were
examined using X-ray diffraction (XRD). The results show that no
clear diffraction peaks in the range 2θ= (20-50)o for the as deposited
films. On the other hand, by annealing the films to 423K in vacuum
for 1 h, a weak reflection peak attributable to cubic NiO was
detected. On heating the films at 473K for 1 h, this peak was
observed to be stronger. The most intense peak is at 2θ = 37

The effect of Wood Flour addition to the gamma alumina powder used in the preparation of gamma alumina (ɤ-Al₂O₃) catalyst carrier extrudates on the pore volume and BET surface area physical properties was investigated. Two parameters which are size of wood flour particles and its quantity were studied. The sizes of wood flour particles used are 150 µm, 212 µm and 500 µm and the weight percentage added to the gamma alumina powder during the preparation of the extrudates are (1%, 3%, 5% and 10%). The results showed that the addition of wood flour to the gamma alumina powder in order to get gamma alumina extrudates used as catalyst carrier is one of the successful methods to improve the pore volume

t. The current study was conducted on the umbilical cord blood of newborns in the Banks Hospital in Baghdad, Diyala, and Khalis in Diyala, where the study included 90 samples of blood, and samples were collected for the period from the 1st of October;2020 to The first of February;2021 AD, where the study included measuring levels of interleukin-6;Adiponectin,glucose and bilirubin in the blood, comparison study between the study variables with the child's weight (greater than 3 kg),(less or equal 3 kg),the mother's age (greater than 25 years, less or equal to 25 years),the sex of the child (male, female).The results of our study showed that there were no significant differences between the variables of the current study between the two sex