Stable isotope (?18O, ?D) values were determined along with the chemical compositions at 10 different locations along the Tigris river between Baghdad-Ammara cities of Iraq. The physico-chemical parameters and isotopic data were measured. The sampling site represents 34 % of total Tigris river in the republic of Iraq. The systematically increased in values of stable isotope as move from the downstream of the river and the most significantly appears at Kut lake. This increase occurs as a result of several factors, viz. (a) evaporation occurs low water level in the river and its tributaries, and (b) return flow water to the river from irrigation water in groundwater systems. The change in ion distribution and in the isotopic values related di

Cefixime (CFX) was treated with sodium nitrite and hydrochloric acid for diazotization reaction followed by coupling with ?-Naphthol in alkaline medium to form, a yellow colored azo dye compound which exhibits maximum absorption (?_max) at 412 nm where the concentration of (CFX) was determined spectrophotometrically. The optimum reaction conditions and other analytical parameters were evaluated. Beer’s law was obeyed in the concentration range of (1-20) ?g.mL^-1 with a molar absorptivity of 34870.5 L.mol^-1.cm^-1. The limit of detection was found to be 0.1090 ?g.mL^-1 and the Sandell's sensitivity value was 0.0130 ?g.cm^-2. The proposed method could be successfully applied to

The data presented in this paper are related to the research article entitled “Novel dichloro(bis{2-[1-(4-methylphenyl)-1H-1,2,3-triazol-4-yl-κN3 ]pyridine-κN})metal(II) coordination compounds of seven transition metals (Mn, Fe, Co, Ni, Cu, Zn and Cd)” (Conradie et al., 2018) [1]. This paper presents characterization and structural data of the 2-(1-(4-methyl-phenyl)-1H-1,2,3-triazol-1-yl)pyridine ligand (L2 ) (Tawfiq et al., 2014) [2] as well as seven dichloro(bis{2- [1-(4-methylphenyl)-1H-1,2,3-triazol-4-yl-κN3 ]pyridine-κN})metal (II) coordination compounds, [M(L2 )2Cl2], all containing the same ligand but coordinated to different metal ions. The data illustrate the shift in IR, UV/VIS, and NMR (for diamagnetic complexes) peaks wh

The meteorite with a single total mass of 630 gm as a visible meteorite has fallen on 22 March 2021, at 10:00 a.m. in Al-Sherqat subdistrict within Salah Al-Din, northern Iraq; and therefore, was named Al-Sherqat meteorite by the authors. It is characterized by a uniform structure of coherent and medium degree of malleability. It is of a well-crystalline structure and not homogeneous in composition. The Al-Sherqat meteorite is composed of metallic phases of 7.6 gm/cm3 density exhibiting an oriented intergrowth of kamacite (α-FeNi) with taenite showing a Widmanstätten pattern on an etched polished section with the finest octahedrite kamacite bandwidth of less than 0.2 mm. It is composed of Fe (86.9 wt%), Ni (9.63 wt%), P (1.31 wt%)

Chemical bath deposition was used to synthesize ZnO nanorods (NRs) on glass and fluorine^_doped tin oxide (FTO) substrates. X-ray diffraction was performed to examine the crystallinity of ZnO nanorod. Results showed that ZnO NRs had a wurtzite crystal structure. Field emission scanning electron microscopy images showed that glass sample had rod-like structure distribution with (50 nm) diameter and average length of approximately (700 nm), whereas the FTO-coated glass sample had 25 nm diameter and average length of approximately 950 nm. The direct optical transition band gaps of the glass and FTO^_coated glass samples were( 4 and 4.43 eV), respectively. The structural and optical properties of the synthesized ZnO p

The effect of annealing temperature (Ta) on the electrical properties like ,D.C electrical conductivity (σ DC), activation energy (Ea),A.C conductivity σa.c ,real and imaginary (ε1,ε2) of dielectric constants ,relaxation time (τ) has been measured of ZnS thin films (350 nm) in thickness which were prepared at room temperature (R.T) using thermal evaporation under vacuum . The results showed that σD.C increases while the activation energy values(Ea) decreases with increasing of annealing temperature.(Ta) from 303- 423 K .
The density of charge carriers (nH) and Hall mobility (μH) increases also with increasing of annealing temperature Hall effect measurements showed that ZnS films were n-type converted to p-type at high annealin

The cement slurry is a mixture of cement, water and additives which is established at the surface for injecting inside hole. The compressive strength is considered the most important properties of slurry for testing the slurry reliability and is the ability of slurry to resist deformation and formation fluids. Compressive strength is governed by the sort of raw materials that include additives, cement structure, and exposure circumstances. In this work, we use micro silica like pozzolanic materials. Silica fume is very fine noncrystalline substantial. Silica fume can be utilized like material for supplemental cementations for increasing the compressive strength and durability of cement. Silica fume has very fine particles size less