Titanium dioxide nanotube arrays (TiO2 NTAs) were successfully decorated with nanoclusters of cobalt by an electrochemical deposition method. This Co-TiO2 NTAs nanostructure exhibited high compatibility with aluminum chloride\ chloroacetamide (an ionic liquid) and calcium chloride dihydrate\ acetamide (a deep eutectic solvent), leading to significant improvements in the electrochemical properties of the system. Significantly, this led to a discernible augmentation in both potential and current values, concomitant with a decrease in internal resistance. The presence of cobalt facilitated a faster transfer of electric charge, enhancing the overall efficiency of the system. Moreover, the incorporation of cobalt exhibited a ben

This paper represents an experimentalattempt to predict the influence of CO2-MAG welding variables on the shape factors of the weld joint geometry. Theinput variables were welding arc voltage, wire feeding speed and gas flow rate to investigate their effects on the shape factorsof the weld joint geometry in terms of weld joint dimensions (bead width, reinforcement height, and penetration). Design of experiment with response surface methodology technique was employed to buildmathematical models for shape factors in terms of the input welding variables. Thepredicted models were found quadratic type and statistically checked by ANOVA analysis for adequacy purpose. Also, numerical and graphical optimizations were carried out

4,4'-(pyridine-2,6-diylbis(1,3,4-oxadiazole-5,2-diyl))bisphenol monomer (3)was synthesized from cyclization of N'2,N'6-bis(4-hydroxybenzylidene)pyridine-2,6-dicarbohydrazide (2)in the presence of bromine in glacialacetic acid. Newly five polymers (P1-P5) were synthesized from reaction bis-1,3,4-oxadiazole bisphenolmonomer with five different di acid chloride. The antibacterial activity of the synthesized polymers was screened against gram positive and gram negative bacteria. Polymers P4 and P5 exhibited significant antibacterial against all microorganisms, as well these polymers showed highest antifungal activity.

This study aimed to evaluate the surface changes of commercial pure Titanium disks (CP Ti) and the Ti 13Nb 13 Zr (Alloy) with a zigzag pattern of laser surface treatment. In vitro, experimental study of CNC Laser treatment on the CP Ti and Alloy disks. Texturing the surfaces of CP Ti and Alloy disks via CNC laser, the sample disks were analyzed using surface roughness, wettability and FESEM. The FESEM revealed a proper increase in the surface texturing and roughness on macro and micro measures without crack formation or dramatic change of the core substance of the CP Ti and Alloy disks. The CNC laser is an effective and suitable method for surface texturing CP Ti and Alloy for dental implantology. Keywords: Commercial pure Titanium;

In this paper, we studied the spark corona discharge in tap and distillited waters. The results show the shape of cone that generated on the tip of capillary tube is different with conductivity of liquids. The blue glow appears at the end of capillary tube and the drop extends into a cone. In addition, the conducitivity is affected on the relationship between the appearance of the blue glow discharge with the applied voltage. The size of the cone decreases with an increase in applied voltage. The cone diameter at the base of capillary tube oscillates with period approximately 1 Sec. this oscillates in the cone diameters is due to the change distance between the liquid electrode and the surface of liquid. The intensity of spark corona dis

Acetophenone sulfamethoxazole and 3-Nitrobenzophenone sulfamethoxazole were prepared from the reaction of sulfamethoxazole with two ketones. The prepared ligands were identified by (C.H.N) analysis and UV-VIS, FT-IR spectroscopic techniques. Metal complexes of the two ligands were prepared in an aqueous alcohol with Zn (II), Mn (II) and Cu (II) ions with a molar ratio1:1. The proposed general formula for the resulting complexes was [ML.CL2.H2O]H2O .The complexes were characterized by (C.H.N) technique , spectroscopic methods ,conductivity, atomic absorption ,magnetic susceptibility measurements and melting point. According to the results obtained, the suggested geometry is to be octahedral for all the complexes.

This study evaluates the flexural behavior of ultra-thin (50 mm) one‑way reinforced‑concrete (RC) slabs retrofitted with near‑surface mounted (NSM) carbon‑fiber‑reinforced polymer (CFRP) rods under quasi‑static loading. T300‑grade CFRP rods (≈4 mm diameter) were bonded in pre‑cut 7 mm × 7 mm grooves using a two‑part epoxy. As a proof-of-concept experimental baseline, three simply‑supported specimens (1000 mm × 500 mm × 50 mm) were tested in a six‑point bending configuration (four applied loads + two reactions): two conventional controls and one strengthened slab. A load‑control rate of ~15 kN/min was applied; the controls were cycled twice and the strengthened slab four times. Relative to the average of

    Synthesis of 2-mercaptobenzothiazole (A₁) is performed from the reaction of  o-aminothiophenol and carbon disulfide CS₂ in ethanol under basic condition. Compound (A₁)  is reacted with chloro acetyl chloride to give compound (A₂). Hydrazide acid compound (A₃) is obtained from the reaction of compound (A₂) with  hydrazine hydrate in ethanol under reflux in the presence of glacial acetic acid .The reaction of hydrazide acid compound (A₃) with ethyl acetoacetate gives pyrazole compound (A₄). The new hydrazone  compound (A₅) was prepared from the reaction of compound (A₃) with  benzaldehyde. Reaction of compound