In this study, geopolymer mortar was designed in various experimental combinations employing 1% micro steel fibers and was subjected to different temperatures, according to the prior works of other researchers. The geopolymer mortar was developed using a variety of sustainable material proportions (fly ash and slag) to examine the influence of fibers on its strength. The fly ash weight percentage was 50%, 60%, and 70% by slag weight to study its effect on the geopolymer mortar's properties. The optimal ratio produced the most significant results when mixed at a 50:50 ratio of fly ash and slag with 1% micro steel fibers at curing temperature 240oC for 4 hours through two days. The compressive strength of the geopolymer mortar increas

Academic chemical laboratories (ACL) are considered public places  the employees come in contact with a variety of pollutants. The aim of the current study was to detect heavy metals levels in the indoor air of ACL in two universities in Baghdad city and assess their levels in the academic employees’ scalp hair as biomarkers. Air samples inside ACL were collected to detect Fe, Cd, Zn, Pb and Cu. Scalp hair samples were collected from 40 adult chemical laboratory employees aged 30-60 years, who worked 5 days/week for 6 hours a day. Personal information relating to employees such as age, duration of exposure, smoking habit and sex, was collected as a questionnaire. The results of this study concluded that academic laboratory employ

Background: Eucalyptus extracts and derivatives are natural substances with potent antimicrobial properties. This study investigated the in- vitro effects of non-nutritive sweeteners on the antifungal activity of alcoholic and aqueous Eucalyptus extracts against Candida albicans, a common oral pathogen. Materials and Method: Ten isolates of Candida albicans were isolated from dental students’ salivary samples. The alcoholic and aqueous extracts were prepared from fresh Eucalyptus leaves using maceration. The sensitivity of Candida albicans isolates to various concentrations of Eucalyptus extracts ranging from 50 to 250 (mg/mL) was evaluated via agar well diffusion method, while the agar streaking method  was used to assess the minimum

Background: Decalcification of surface enamel adjacent to fixed orthodontic appliances, in the form of white spot lesions, is a wide spread and familiar well-known side effect of orthodontic treatment. The present study was carried out to evaluate the effect of enamel protective agent (Clinpro white varnish) on shear and tensile bond strength of Dentaurum orthodontic stainless steel brackets by using 3M Unitek and Ormco as orthodontic adhesive agents. Materials and methods: Sixty-four extracted human upper first premolar teeth were selected and randomly divided into two groups with 32 teeth each, representing the shear and tensile bond strength testing groups. Then according to the type of bonding adhesive and the addition of Clinpro before

            A simple, rapid, accurate and sensitive spectrophotometric method for the determination of thiaminehydrochloride has been developed. The method is based on the formation of the Schiff’s base between the primary amino group present in thiamine hydrochloride and aldehyde group present in the vanillin reagent to produce a yellow colored complex having maximum absorption at 390 nm. Beer^’s law has obeaid over the concentration range of 2-28µg/mL, with molar absorptivity of 0.96x10⁴L/mol.cm. The average recovery which is a measure of accuracy is 100±1.3% and the relative standard deviation (RSD) is less than1.5 .The present method is considered to be

A simple, rapid and sensitive spectrophotometirc method for the determination of trace amounts of promethazine hydrochloride in the aqueous solution is described. The method is based on the complexation of promethazine hydrochloride with In (III) in the presence of sodium hydroxide to form an soluble product with maximum absorption at 304nm. Beer’s law is obeyed over the concentration range of (2- 20μg/ml) with molar absorptivity of (1.92× 103 L.mol-1 .cm -1 ). The optimum conditions for all development are described and the proposed method has been successfully applied for the determination of promethazine hydrochloride in bulk drug.

a simple accurate and sensitive spectrophotometric method for the determination of promethazine HCI has been developed the method is based on the oxidative coupling reaction of promethazine

The corrosion inhibition of low carbon steel in1N HCl solution in the presence of peach juice at temperature (30,40,50,and 60)°C at concentration ( 5, 10, 20, 30, 40and 50 cm3/L)were studied using weight loss and polarization techniques. Results show that the inhibition efficiency was increased with the increase of inhibitor concentration and increased with the increase of temperature up to 50ºC ,above 50ºC (i.e. at 60 ºC) the values of efficiency decreases. Activation parameters of the corrosion process such as activation energies, Ea, activation enthalpies, ΔH, and activation entropies, ΔS, were calculated. The adsorption of inhibitor follows Langmuir isotherm. Maximum inhibition efficiency obtained was a bout 91% at 50ºC in the

In this work was prepared three different types of modified screen printed carbon electrode (SPCEs) with drops casted method, the used carbone nanomaterials were the MWCNT, functionalized –MWCNT (f-MWCNT) and After several experiments were made to find an appropriate ratio to make good GOT/f-MWCNT nanocomposite, and found the suspension mixture (1:1) from GOT/f-MWCNT (f-MWCNT-GOT). The electrical and physical properties were performed with cyclic voltammeter technique, and studied the maximum current response, the effective surface area, effect of the pH value and the determination of active surface area for MWCNT-SPCE , f-MWCNT-SPCE and f-MWCNT-GOT/SPCE as (0.04 cm2), (0.119 cm2) and (0.115 cm2) respectively, the surface coverage concent