The ABO blood group system is highly polymorphic, with more than 20 distinct sub-groups; study findings are usually related to ABO phenotype, but rarely to the ABO genotype and animal models are unsatisfactory because their antigen glycosylation structure is different from humans. Both the ABO and Rh blood group systems have been associated with a number of diseases, but this is more likely related to the presence or absence of these tissue antigens throughout the body and not directly or primarily related to their presence on RBCs. A total of fifty-two 52 patients without complication of DMII, two hundred sixteen 216 patients with complication of DMII and seventy-one 71 person as healthy control were included in the study. The resu

One hundred twelve urine samples were collected from Baghdad hospitals and examined by different identification techniques. Seventy isolates (62.5%) were diagnosed as Escherichia coli after microscopic and cultural identifications. The result of PCR product electrophoresis on the isolates showed that thirteen isolates (18.57%) have Pap E gene which are uropathogenic E. coli. Antibiotic susceptibility test was done, and four high resistant strains were mixed with aqueous extract of Quercus infectoria plant in 96 well ELISA plate and incubated for different times. After 0, 6, and 12 hr. of incubation, the effect of the plant extract on the bacterial growth was determined by ELISA reader, and the effect on the expression of P

Zinc Oxide (ZnO) thin films of different thickness were prepared
on ultrasonically cleaned corning glass substrate, by pulsed laser
deposition technique (PLD) at room temperature. Since most
application of ZnO thin film are certainly related to its optical
properties, so the optical properties of ZnO thin film in the
wavelength range (300-1100) nm were studied, it was observed that
all ZnO films have high transmittance (˃ 80 %) in the wavelength
region (400-1100) nm and it increase as the film thickness increase,
using the optical transmittance to calculate optical energy gap (Eg
opt)
show that (Eg
opt) of a direct allowed transition and its value nearly
constant (~ 3.2 eV) for all film thickness (150

In this research a local adsorbent was prepared from waste tires using two-step pyrolysis method. In the carbonization process, nitrogen gas flow rate was 0.2L/min at carbonization temperature of 500ºC for 1h. The char products were then preceded to the activation process at 850°C under carbon dioxide (CO2) activation flow rate of 0.6L/min for 3h. The activation method produced local adsorbent material with a surface area and total pore volume as high as 118.59m2 /g and 0.1467cm3/g, respectively. The produced . local adsorbent (activated carbon) was used for adsorption of lead from aqueous solution. The continuous fixed bed column experiments were conducted. The adsorption capacity performance of prepared activated carbons in this work

In this paper, a simulation of the electrical performance for Pentacene-based top-contact bottom-gate (TCBG) Organic Field-Effect Transistors (OFET) model with Polymethyl methacrylate (PMMA) and silicon nitride (Si3N4) as gate dielectrics was studied. The effects of gate dielectrics thickness on the device performance were investigated. The thickness of the two gate dielectric materials was in the range of 100-200nm to maintain a large current density and stable performance. MATLAB simulation demonstrated for model simulation results in terms of output and transfer characteristics for drain current and the transconductance. The layer thickness of 200nm may result in gate leakage current points to the requirement of optimizing the t

Experimental investigations had been done in this study to demonstrate the effect of natural particles used as a reinforcement material to unsaturated polyester resin. The tensile test and water absorption were investigated according to (ASTM D638) and (ASTM D570), respectively. The influence of sunflower husk and pomegranate husk particles, used as a reinforcement material, on the tensile strength, Young's modulus and water absorption with different weight fraction (3%, 7% and 10%) and particle grain size (50µm, 100 µm and 150 µm), has been investigated. The water absorption of polymer composites was studied by measuring the specimen weight before and after immersion in water for one hundred days. In the experiments of tensile test,